Aqueous iron carbohydrate complexes, their production and medicaments containing them

ABSTRACT

A water soluble iron carbohydrate complex obtainable from an aqueous solution of iron(III) salt and an aqueous solution of the oxidation product of one or more maltrodextrins using an aqueous hypochlorite solution at a pH-value within the alkaline range, where, when one maltodextrin is applied, its dextrose equivalent lies between 5 and 20, and when a mixture of several maltodextrins is applied, the dextrose equivalent of the mixture lies between 5 and 20 and the dextrose equivalent of each individual maltodextrin contained in the mixture lies between 2 and 40, a process for its production and a medicament for the treatment and prophylaxis of iron deficiency conditions.

This application is a continuation of U.S. application Ser. No. 16/389,234 filed on Apr. 19, 2019, which is a continuation of U.S. application Ser. No. 13/835,400, filed on Mar. 15, 2013, now U.S. Pat. No. 10,519,252, which is a continuation of U.S. application Ser. No. 13/556,733, filed on Jul. 24, 2012, now U.S. Pat. No. 9,376,505, which is a continuation of U.S. application Ser. No. 12/581,212, filed on Oct. 19, 2009, now abandoned, which is a divisional of U.S. application Ser. No. 10/531,895, filed on Oct. 20, 2003, now U.S. Pat. No. 7,612,109, and which is a National Stage of Application No. PCT/EP2003/011596, filed Oct. 20, 2003, which claims the benefit of German Application No. 10249552.1, filed on Oct. 23, 2002. These applications are herein incorporated by reference into the present application.

The present invention concerns water-soluble iron carbohydrate complexes which are used for the treatment of iron deficiency anemia, their preparation, medicaments containing them and their use for the prophylaxis or treatment of iron deficiency anemia. The medicaments are especially useful for parenteral application.

Iron deficiency anemia can be treated or prophylactically treated by the application of medicaments containing iron. In this respect the use of iron carbohydrate complexes is known. A water soluble iron (III) hydroxide sucrose complex is a frequently and successfully used preparation (Danielson, Salmonson, Derendorf, Geisser, Drug Res., Vol. 46: 615-621, 1996). It is also known in the art to use, for parenteral application, iron dextran complexes as well as complexes based on pullulans (WO 02/46241), which are difficult to obtain and have to be produced under pressure at high temperatures and involving hydrogenating steps. Other iron carbohydrate complexes are also known for oral application.

The problem to be solved by the present invention is to provide an iron preparation which is especially to be applied parenterally and which can easily be sterilized; the known parenterally applicable preparations on the basis of sucrose and dextran were only stable at temperatures up to 100° C., which made sterilization difficult. Further, the preparation to be provided by the invention shall have reduced toxicity and shall avoid dangerous anaphylactic shocks which can be induced by dextran. Also, the stability of the complexes of the preparation shall be high in order to enable a high applicable dosage and a high rate of application. Furthermore, the iron preparation is to be producible from easily obtainable starting products and without great effort.

In accordance with the present invention the problem can be solved by providing iron (III) carbohydrate complexes on the basis of the oxidation products of maltodextrins.

Therefore, an object of the present invention is water soluble iron carbohydrate complexes, which are obtainable from an aqueous solution of an iron (III) salt and an aqueous solution of the oxidation product of one or more maltodextrins, using an aqueous hypochlorite solution at an alkaline pH value, e.g., of 8 to 12 where, when one maltodextrin is applied, its dextrose equivalent lies between 5 and 20, and when a mixture of several maltodextrins is applied, the dextrose equivalent of the mixture lies between 5 and 20 and the dextrose equivalent of each individual maltodextrin contained in the mixture lies between 2 and 40.

A further object of the present invention is a process for producing the iron carbohydrate complexes according to the invention wherein one or more maltodextrins are oxidized in an aqueous solution at an alkaline pH value, e.g., of 8 to 12 using an aqueous hypochlorite solution and reacting the obtained solution with an aqueous solution of an iron (III) salt where, when one maltodextrin is applied, its dextrose equivalent lies between 5 and 20, and when a mixture of several maltodextrins is applied, the dextrose equivalent of the mixture lies between 5 and 20 and the dextrose equivalent of each individual maltodextrin contained in the mixture lies between 2 and 40.

The usable maltodextrins are easily obtainable starting products, and they are commercially available.

In order to prepare the ligands of the complexes of the invention, the maltodextrins are oxidized in an aqueous solution with a hypochlorite solution. Suitable examples are solutions of alkali hypochlorites such as a solution of sodium hypochlorite. Commercially available solutions can be used. The concentration of the hypochlorite solution, e.g., is at least 13% by weight, preferably on the order of 13 to 16% by weight, calculated as active chlorine. Preferably the solutions are used in such an amount that about 80 to 100%, preferably about 90%, of one aldehyde group per molecule of maltodextrin is oxidized. In this manner, the reactivity caused by the glucose content of the maltodextrin molecules is lowered to 20% or less, preferably to 10% or less.

The oxidation is carried out in an alkaline solution, e.g., at a pH of 8 to 12, for example 9 to 11. As an example, oxidation can be carried out at temperatures on the order of 15 to 40° C., preferably of 25 to 35° C. The reaction times are, e.g, on the order of 10 minutes to 4 hours, e.g., 1 to 1.5 hours.

By this procedure the degree of depolymerization of the starting maltodextrins is kept at a minimum. Only theoretically it is assumed that the oxidation occurs mainly at the terminal aldehyde group (acetal or semiacetal group, respectively) of the maltodextrin molecules.

It is also possible to catalyze the oxidation reaction of the maltodextrins. The addition of bromide ions is suitable, e.g., in the form of alkali bromides, for example sodium bromide. The added amount of bromide is not critical. The amount is kept as low as possible in order to achieve an end product (Fe-complex) which can easily be purified. Catalytic amounts are sufficient. As stated above, the addition of bromide is possible, however, not necessary.

Further, it is also possible to use other oxidation systems, such as, e.g., the known ternary oxidation system hypochlorite/alkali bromide/2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO) for the oxidation of the maltodextrins. The process to oxidize maltodextrins catalytically with alkali bromides or with the ternary TEMPO system is described, e.g., by Thaburet et al, in Carbohydrate Research 330 (2001) 21-29, which method can be used for the present invention,

In order to prepare the complexes of the invention, the obtained oxidized maltodextrins are reacted with an iron (III) salt in an aqueous solution. In order to do so, the oxidized maltodextrins can be isolated and redissolved. It is also possible, however, to use the obtained aqueous solutions of the oxidized maltodextrins directly for the further reaction with the aqueous iron (III) solutions.

Water soluble salts of inorganic or organic acids, or mixtures thereof, such as halides, e.g., chloride and bromide, or sulfates can be used as iron (III) salts. It is preferred to use physiologically acceptable salts. It is especially preferred to use an aqueous solution of iron (III) chloride.

It has been found that the presence of chloride ions favors the formation of the complexes. The chloride ions can be used in the form of water soluble chlorides such as alkali metal chlorides, e.g., sodium chloride, potassium chloride or ammonium chloride. As stated, the iron (III) is preferably used in the form of the chloride.

For instance, the aqueous solution of the oxidized maltodextrin can be mixed with an aqueous solution of the iron (III) salt in order to carry out the reaction. Here, it is preferred to proceed in a manner so that during and immediately after mixing the oxidized maltodextrin and the iron (III) salt, the pH is strongly acid or so low that no hydrolysis of the iron (III) salt occurs, e.g., pH 2 or less, in order to avoid an undesired precipitation of iron hydroxides. In general, it is not necessary to add an acid, if iron (III) chloride is used, since aqueous solutions of iron (III) chloride can be sufficiently acidic. Only after mixing, the pH is raised to values, e.g., on the order of at least 5, for example, up to 11, 12, 13 or 14. The pH is preferably raised slowly or gradually which, for example, can be achieved by first adding a weak base, for example, up to a pH of about 3, and then neutralizing further using a stronger base. Examples of weak bases are alkali—or alkaline earth—carbonates, bicarbonates, such as sodium and potassium carbonate or bicarbonate, or ammonia. Examples of strong bases are alkali—or alkaline earth—hydroxides such as sodium, potassium, calcium or magnesium hydroxide.

The reaction can be improved by heating. For example, temperatures on the order of 15° C. up to boiling point can be used. It is preferred to raise the temperature gradually. Thus, for example, it is possible to heat to about 15 to 70° C. and then raise the temperature gradually up to boiling point.

The reaction times are, for example, on the order of 15 minutes up to several hours, e.g., 20 minutes to 4 hours, such as 25 to 70 minutes, e.g., 30 to 60 minutes.

The reaction can be carried out in a weakly acid range, for example, at a pH on the order of 5 to 6. However, it has been found, that it is useful, but not necessary, to raise the pH during the formation of the complexes to higher values of up to 11, 12, 13 or 14. In order to complete the reaction, the pH can be lowered then by addition of an acid, for example, to the order of 5 to 6. It is possible to use inorganic or organic acids or a mixture thereof, especially hydrogen halide acids such as hydrogen chloride or aqueous hydrochloric acid, respectively.

As stated above, the formation of the complexes is usually improved by heating. Thus, at the preferred embodiment of the invention, wherein the pH is raised during the reaction to ranges of at least 5 and above, up to 11 or 14, it is, for instance, possible to work at first at lower temperatures on the order of 15 to 70° C., such as 40 to 60° C., e.g., about 50° C., whereafter the pH is reduced to values on the order of at least 5, and the temperature is gradually raised over 50° C. up to boiling point

The reaction times are on the order of 15 minutes up to several hours and they can vary depending on the reaction temperature. If the process is carried out with an intermediate pH of more than 5, it is, for example, possible to work 15 to 70 minutes, e.g., 30 to 60 minutes, at the enhanced pH, for example, at temperatures of up to 70° C., whereafter the pH is lowered to a range on the order of at least 5 and the reaction is carried out for a further 15 to 70 minutes, e.g., 30 to 60 minutes, at temperatures, e.g., up to 70° C., and optionally a further 15 to 70 minutes, e.g., 30 to 60 minutes, at higher temperatures up to boiling point.

After the reaction the obtained solution can be cooled, e.g., to room temperature and can optionally be diluted and optionally be filtered. After cooling, the pH can be adjusted to the neutral point or a little below, for example, to values of 5 to 7, by the addition of an acid or base. It is possible to use, e.g., the acids and bases which have been mentioned for carrying out the reaction. The solutions obtained are purified and can directly be used for the production of medicaments. However, it is also possible to isolate the iron (III) complexes from the solution, e.g., by precipitation with an alcohol such as an alkanol, for example, ethanol. Isolation can also be effected by spray-drying. Purification can take place in the usual way, especially in order to remove salts. This can, for example, be carried out by reverse osmosis. It is, for example, possible to carry out the reverse osmosis before spray-drying or before a direct application in medicaments.

The iron content of the obtained iron (III) carbohydrate complexes is, for example, 10 to 40% weight/weight, especially, 20 to 35% weight/weight. They can easily be dissolved in water. It is possible to prepare neutral aqueous solutions which, e.g., have an iron content of 1% weight/vol. to 20% weight/vol. Such solutions can be sterilized thermically. The weight average molecular weight of the obtained complexes, is, for example, 80 kDa to 400 kDa, preferably 80 kDa to 350 kDa, especially preferred up to 300 kDa (measured by gel permeation chromatography, e.g., as described by Geisser et al, in Arzneim. Forsch/Drug Res. 42(II), 12, 1439-1452 (1992), paragraph 2.2.5).

As stated above, it is possible to provide aqueous solutions from the complexes of the invention. These solutions are especially useful for parenteral application. However, it is also possible to apply them orally or topically. Contrary to the known parenterally applicable iron preparations, they can be sterilized at high temperatures, e.g., at 121° C. and above, at short contact times of, e.g., 15 minutes, by acquiring F₀≥15. The contact times are correspondingly shorter at higher temperatures. Preparations hitherto known had to be sterilely filtrated and mixed with preservatives, such as benzyl alcohol or phenol. Such additives are not necessary in the invention. Hence, it is possible to fill the solutions of the complexes, for example, into ampoules. It is, for example, possible to fill solutions having a content of 1 to 20% by weight, e.g., 5% by weight, into vessels such as ampoules or phials, e.g., of 2 to 100 ml, e.g., up to 50 ml. The preparation of the parenterally applicable solutions can be carried out as known in the art, optionally using additives which are normally used for parenteral solutions. The solutions can be formulated in such a way that they can be administered by injection or in the form of an infusion, e.g., in brine solution. For the oral or topical application it is possible to formulate preparations with usual excipients and additives.

Thus, a further object of the invention is aqueous medicaments which are especially useful for the parenteral, intravenous but also intramuscular application, as well as for oral or topical application. The aqueous medicaments are especially useful for the treatment of iron deficiency anemia. A further object of the invention is also the use of the iron (III) carbohydrate complexes according to the invention for the treatment and prophylaxis of iron deficiency anemia or the production of medicaments especially for the parenteral treatment of iron deficiency anemia. The medicaments can be used in human and veterinary medicine.

The advantages which are achieved with the iron (III) carbohydrate complexes of the invention are the above-mentioned high sterilization temperatures, as well as the low toxicity and the reduced danger of anaphylactic shock. The toxicity of the complexes according to the invention is very low. The LD₅₀ lies at over 2000 mg Fe/kg, compared to the LD₅₀ of the known pullulan complexes, which lies at 1400 mg Fe/kg. In view of the high stability of the complexes of the invention, it is possible to enhance the rates of application as well as the dosages. Thus, it is possible to apply the medicaments of the invention parenterally in the form of a single dose. Such a single dose is, for example, 500 to 1000 mg iron. The dose can be applied, for example, during the course of one hour. A further advantage lies in the high degree of availability of the maltodextrins used as starting products, which are, e.g., commercially available additives in the food processing industry.

In the present description, as well as in the following examples, the dextrose equivalents are measured gravimetrically. In order to do so, the maltodextrins are reacted in a boiling aqueous solution with Fehling's solution. The reaction is carried out quantitatively, i.e. until the Fehling's solution is no longer discolored. The precipitated copper (I) oxide is dried at 105° C. until a constant weight is achieved and measured gravimetrically. The glucose content (dextrose equivalent) is calculated from the obtained results as % weight/weight of the maltodextrin dry substance. It is, for example, possible to use the following solutions: 25 ml Fehling's solution I, mixed with 25 ml Fehling's solution II; 10 ml aqueous maltodextrin solution (10% mol/vol) (Fehling's solution I: 34.6 g copper (II) sulfate dissolved in 500 ml water; Fehling's solution II: 173 g potassium sodium tartrate and 50 g sodium hydroxide dissolved in 400 ml water).

EXAMPLE 1

100 g maltodextrin (9.6 dextrose equivalent measured gravimetrically) are dissolved by stirring in 300 ml water at 25° C. and oxidized by addition of 30 g sodium hypochlorite solution (13 to 16 weight percent active chlorine) at pH 10.

At first, the oxidized maltodextrin solution and then 554 g sodium carbonate solution (17.3% weight/weight) are added at room temperature to 352 g of a stirred iron (Ill) chloride solution (12% weight by weight Fe).

Then, the pH is adjusted to 11 by addition of sodium hydroxide, and the solution is heated to 50° C. and kept at 50° C. for 30 minutes. Then, acidification to a pH of 5 to 6 is effected by addition of hydrochloric acid, the solution is kept at 50° C. for a further 30 minutes and then heated to 97-98° C., and the temperature is kept for 30 minutes at this range. After cooling the solution to room temperature, the pH is adjusted to 6-7 by the addition of sodium hydroxide.

The solution is then filtered through a sterilization filter and then examined for sediments. Thereafter, the complex is isolated by precipitation with ethanol in a range of 1:0.85, and then dried in vacuum at 50° C.

The yield is 125 g (corresponding to 87% of the theoretical value) of a brown amorphic powder having an iron content of 29.3% weight/weight (measured complexometrically).

Molecular weight mw 271 kDa.

EXAMPLE 2

200 g maltodextrin (9.6 dextrose equivalent measured gravimetrically) are dissolved by stirring in 300 ml water at 25° C. and oxidized by addition of 30 g sodium hypochlorite solution (13 to 16 weight percent active chlorine) at pH 10.

At first, the oxidized maltodextrin solution and then 554 g sodium carbonate solution (17.3% weight/weight) are added at room temperature to 352 g of a stirred iron (III) chloride solution (12% weight by weight Fe).

Then, the pH is adjusted to 11 by addition of sodium hydroxide, and the solution is heated to 50° C. and kept for 30 minutes at 50° C. Then, acidification to a pH of 5 to 6 is effected by addition of hydrochloric acid, the solution is kept at 50° C. for a further 30 minutes and then heated to 97-98° C., and the temperature Is kept for 30 minutes at this range. After cooling the solution to room temperature, the pH is adjusted to 6-7 by the addition of sodium hydroxide.

The solution is then filtered through a sterilization filter and then examined for sediments. Thereafter, the complex is isolated by precipitation with ethanol in a range of 1:0.85, and then dried in vacuum at 50° C.

The yield is 123 g (corresponding to 65% of the theoretical value) of a brown amorphic powder having an iron content of 22.5% weight/weight (measured complexometrically).

Molecular weight mw 141 kDa,

EXAMPLE 3

100 g maltodextrin (9.6 dextrose equivalent measured gravimetrically) are dissolved by stirring in 300 ml water at 25° C. and oxidized by addition of 30 g sodium hypochlorite solution (13 to 16 weight percent active chlorine) and 0.7 g sodium bromide at pH 10.

At first, the oxidized maltodextrin solution and then 554 g sodium carbonate solution (17.3% weight/weight) are added at room temperature to 352 g of a stirred iron (Ill) chloride solution (12% weight by weight Fe).

Then, the pH is adjusted to 6.5 by addition of sodium hydroxide and the solution is heated to 50° C. and kept for 60 minutes at 50° C. Then, acidification to a pH of 5 to 6 is effected by addition of hydrochloric acid, the solution is kept at 50° C. for a further 30 minutes and then heated to 97-98° C., and the temperature is kept for 30 minutes at this range. After cooling the solution to room temperature the pH is adjusted to 6-7 by the addition of sodium hydroxide.

The solution is then filtered through a sterilization filter and then examined for sediments. Thereafter, the complex is isolated by precipitation with ethanol in a range of 1:0.85 and then dried in vacuum at 50° C.

The yield is 139 g. (corresponding to 88% of the theoretical value) of a brown amorphic powder having an iron content of 26.8% weight/weight (measured complexometrically).

Molecular weight mw 140 kDa.

EXAMPLE 4

A mixture of 45 g maltodextrin (6.6 dextrose equivalent measured gravimetrically) and 45 g maltodextrin (14.0 dextrose equivalent measured gravimetrically) is dissolved by stirring in 300 ml water at 25° C. and oxidized by addition of 25 g sodium hypochlorite solution (13 to 16 weight percent active chlorine) and 0.6 g sodium bromide at pH 10.

At first, the oxidized maltodextrin solution and then 554 g sodium carbonate solution (17.3% weight/weight) are added at room temperature to 352 g of a stirred iron (Ill) chloride solution (12% weight by weight Fe).

Then, the pH is adjusted to 11 by addition of sodium hydroxide and the solution is heated to 50° C. and kept for 30 minutes at 50° C. Then, acidification to a pH of 5 to 6 is effected by addition of hydrochloric acid, the solution is kept at 50° C. for a further 30 minutes and then heated to 97-98° C., and the temperature is kept for 30 minutes at this range. After cooling the solution to room temperature the pH is adjusted to 6-7 by the addition of sodium hydroxide.

The solution is then filtered through a sterilization filter and then examined for sediments. Thereafter, the complex is isolated by precipitation with ethanol in a range of 1:0.85 and then dried in vacuum at 50° C.,

The yield is 143 g (corresponding to 90% of the theoretical value) of a brown amorphic powder having an iron content of 26.5% weight/weight (measured complexometrically).

Molecular weight mw 189 kDa,

EXAMPLE 5

90 g maltodextrin (14.0 dextrose equivalent measured gravimetrically) are dissolved by stirring in 300 ml water at 25° C. and oxidized by addition of 35 g sodium hypochlorite solution (13 to 16 weight percent active chlorine) and 0.6 g sodium bromide at pH 10.

At first, the oxidized maltodextrin solution and then 554 g sodium carbonate solution (17.3% weight/weight) are added at room temperature to 352 g of a stirred iron (Ill) chloride solution (12% weight by weight Fe).

Then, the pH is adjusted to 11 by addition of sodium hydroxide and the solution is heated to 50° C. and kept for 30 minutes at 50° C. Then, acidification to a pH of 5 to 6 is effected by addition of hydrochloric acid, the solution is kept at 50° C. for a further 30 minutes and then heated to 97-98° C. and the temperature is kept for 30 minutes at this range. After cooling the solution to room temperature the pH is adjusted to 6-7 by the addition of sodium hydroxide.

The solution is then filtered through a sterilization filter and then examined for sediments. Thereafter, the complex is isolated by precipitation with ethanol in a range of 1:0.85 and then dried in vacuum at 50° C.

The yield is 131 g (corresponding to 93% of the theoretical value) of a brown amorphic powder having an iron content of 29.9% weight/weight (measured complexometrically).

Molecular weight mw 118 kDa.

EXAMPLE 6

A mixture of 45 g maltodextrin (5.4 dextrose equivalent measured gravimetrically) and 45 g maltodextrin (18.1 dextrose equivalent measured gravimetrically) is dissolved by stirring in 300 ml water at 25° C. and oxidized by addition of 31 g sodium hypochlorite solution (13 to 16 weight percent active chlorine) and 0.7 g sodium bromide at pH 10.

At first, the oxidized maltodextrin solution and then 554 g sodium carbonate solution (17.3% weight/weight) are added at room temperature to 352 g of a stirred iron (Ill) chloride solution (12% weight by weight Fe).

Then, the pH is adjusted to 11 by addition of sodium hydroxide and the solution is heated to 50° C. and kept for 30 minutes at 50° C. Then, acidification to a pH of 5 to 6 is effected by addition of hydrochloric acid, the solution is kept at 50° C. for a further 30 minutes and then heated to 97-98° C. and the temperature is kept for 30 minutes at this range. After cooling the solution to room temperature the pH is adjusted to 6-7 by the addition of sodium hydroxide.

The solution is then filtered through a sterilization filter and then examined for sediments. Thereafter, the complex is isolated by precipitation with ethanol in a range of 1:0.85 and then dried in vacuum at 50° C.

The yield is 134 g (corresponding to 88% of the theoretical value) of a brown amorphic powder having an iron content of 27.9% weight/weight (measured complexometrically).

Molecular weight mw 178 kDa.

EXAMPLE 7

100 g maltodextrin (9.6 dextrose equivalent measured gravimetrically) are dissolved by stirring in 300 ml water at 25° C. and oxidized by addition of 29 g sodium hypochlorite solution (13 to 16 weight percent active chlorine) and 0.7 g sodium bromide at pH 10.

At first, the oxidized maltodextrin solution and then 554 g sodium carbonate solution (17.3% weight/weight) are added at room temperature to 352 g of a stirred iron (Ill) chloride solution (12% weight by weight Fe).

Then, the pH is adjusted to 11 by addition of sodium hydroxide and the solution is heated to 50° C. and kept for 30 minutes at 50° C. Then, acidification to a pH of 5 to 6 is effected by addition of hydrochloric acid, the solution is kept at 50° C. for a further 70 minutes. After cooling the solution to room temperature the pH is adjusted to 6-7 by the addition of sodium hydroxide.

The solution is then filtered through a sterilization filter and then examined for sediments. Thereafter, the complex is isolated by precipitation with ethanol in a range of 1:0.85 and then dried in vacuum at 50° C.

The yield is 155 g (corresponding to 90% of the theoretical value) of a brown amorphic powder having an iron content of 24.5% weight/weight (measured complexometrically).

Molecular weight mw 137 kDa.

EXAMPLE 8

126 g maltodextrin (6.6 dextrose equivalent measured gravimetrically) are dissolved by stirring in 300 ml water at 25° C. and oxidized by addition of 24 g sodium hypochlorite solution. (13 to 16 weight percent active chlorine) and 0.7 g sodium bromide at pH 10.

At first, the oxidized maltodextrin solution and then 554 g sodium carbonate solution (17.3% weight/weight) are added at room temperature to 352 g of a stirred iron (III) chloride solution (12% weight by weight Fe).

Then, the pH is adjusted to 11 by addition of sodium hydroxide and the solution is heated to 50° C. and kept for 30 minutes at 50° C. Then, acidification to a pH of 5 to 6 is effected by addition of hydrochloric acid, the solution is kept at 50° C. for a further 70 minutes. After cooling the solution to room temperature the pH is adjusted to 6-7 by the addition of sodium hydroxide.

The solution is then filtered through a sterilization filter and then examined for sediments. Thereafter, the complex is isolated by precipitation with ethanol in a range of 1:0.85 and then dried in vacuum at 50° C.

The yield is 171 g (corresponding to 86% of the theoretical value) of a brown amorphic powder having an iron content of 21.35% weight/weight (measured complexometrically),

Molecular weight mw 170 kDa.

Comparative Test

In the following, the characteristics of the iron carbohydrate complexes are compared with a commercially available iron sucrose complex. It can be seen that the iron content can be enhanced, the thermal treatment can be carried out at higher temperatures and the toxicity (LD₅₀) can be lowered in accordance with the invention.

According to the Iron hydroxide/ invention sucrose complex Fe content [%] 5.0 2.0 pH 5-7 10.5-11.0 mw [kDa]¹  80-350 34-54 Thermal treatment 121° C./15′ 100° C./35′ LD₅₀ i.v., w.m. [mg >2000 >200 Fe/kg body weight] 

The invention claimed is:
 1. An iron (III) carboxymaltodextrin complex wherein said iron (III) carboxymaltodextrin complex comprises polynuclear iron (III)-hydroxide 4(R)-(poly-(1→4)-O-α-D-glucopyranosyl)-oxy-2(R),3(R),5(R),6-tetrahydroxy-hexanoate and has a weight average molecular weight in the range of from 118 kDa to 271 kDa as measured by gel permeation chromatography, and wherein said 4(R)-(poly-(1→4)-O-α-D-glucopyranosyl)-oxy-2(R),3(R),5(R),6-tetrahydroxy-hexanoate is derived from the oxidation of maltodextrin, wherein when one maltodextrin is applied its dextrose equivalent lies between 5 and 20, and when a mixture of several maltodextrins is applied, the dextrose equivalent of the mixture lies between 5 and 20 and the dextrose equivalent of each individual maltodextrins contained in the mixture lies between 2 and
 40. 2. The iron (III) carboxymaltodextrin complex of claim 1, wherein the oxidized maltodextrin is obtained by oxidation of maltodextrin in an aqueous hypochlorite solution.
 3. A medicament comprising the iron (III) carboxymaltodextrin complex of claim 1 and at least one pharmaceutically acceptable carrier, excipient, or additive, wherein said medicament is an aqueous solution of said iron (III) carboxymaltodextrin complex.
 4. The medicament of claim 3, wherein said iron (III) carboxymaltodextrin complex is present in said aqueous solution in an amount of from 1% to 20% by weight, based on a total weight of the aqueous solution.
 5. The medicament comprising the iron (III) carboxymaltodextrin complex of claim 3, wherein the oxidized maltodextrin is obtained by oxidation of maltodextrin in an aqueous hypochlorite solution.
 6. The medicament comprising the iron (III) carboxymaltodextrin complex of claim 5, wherein said iron (III) carboxymaltodextrin complex is present in said aqueous solution in an amount of from 1% to 20% by weight, based on a total weight of the aqueous solution.
 7. The medicament of claim 3, wherein the aqueous solution has been sterilized at a temperature of 121° C. and above.
 8. The medicament of claim 4, wherein the aqueous solution has been sterilized at a temperature of 121° C. and above.
 9. The medicament of claim 5, wherein the aqueous solution has been sterilized at a temperature of 121° C. and above.
 10. The medicament of claim 6, wherein the aqueous solution has been sterilized at a temperature of 121° C. and above.
 11. The medicament of claim 4 for parenteral administration to a subject in need thereof in the form of a single dose of 500 mg to 1000 mg of iron.
 12. The medicament of claim 8 for parenteral administration to a subject in need thereof in the form of a single dose of 500 mg to 1000 mg of iron.
 13. The medicament of claim 9 for parenteral administration to a subject in need thereof in the form of a single dose of 500 mg to 1000 mg of iron.
 14. The medicament of claim 10 for parenteral administration to a subject in need thereof in the form of a single dose of 500 mg to 1000 mg of iron.
 15. The medicament of claim 4, wherein the iron (III) carboxymaltodextrin complex has a weight average molecular weight of: about 141,000 Da, or about 140,000 Da, or about 189,000 Da, or about 178,000 Da, or about 137,000 Da, or about 170,000 Da.
 16. The medicament of claim 6, wherein the iron (III) carboxymaltodextrin complex has a weight average molecular weight of: about 141,000 Da, or about 140,000 Da, or about 189,000 Da, or about 178,000 Da, or about 137,000 Da, or about 170,000 Da.
 17. The medicament of claim 10, wherein the iron (III) carboxymaltodextrin complex has a weight average molecular weight of: about 141,000 Da, or about 140,000 Da, or about 189,000 Da, or about 178,000 Da, or about 137,000 Da, or about 170,000 Da.
 18. A method for treating an iron deficiency condition in a subject in need thereof, the method comprising administering to the subject in need thereof a pharmaceutically effective amount of a medicament of claim 3, wherein the iron deficiency condition is anemia.
 19. The method of claim 18, wherein said medicament is administered (i) intravenously, (ii) by injection, or (iii) by infusion.
 20. The method of claim 18, wherein the subject is a human.
 21. The method of claim 19, wherein the subject is a human. 